Titanium KSTI-1,2 ASNEX
Titan KSTI-1,2 ASNEX, oxidation-resistant, corrosion-resistant, very good cold formability
KSTI-1,2 ASNEX was developed for high performance automotive and motorcycle exhaust systems and is based on pure titanium that is stabilized using aluminum, silicon and niobium additives. This pure titanium-based grade features excellent fatigue properties and high oxidation resistance at temperatures up to 700-800°C. The higher oxidation resistance enables the use of thinner walls, which saves additional weight and increases the longevity of the system. KSTI-1,2 ASNEX can thus offer a decisive competitive advantage in motorsports.
Areas of application for KSTI-1,2 ASNEX
Exhaust systems for automobiles and motorcycles
Contact us if you have any questions.
S+D METALS KontaktAvailable from stock in the following dimensions
- 0,70 x 1000,00 mm
- 0,80 x 1250,00 mm
- 0,90 x 1250,00 mm
- 1,00 x 1250,00 mm
- 1,20 x 1250,00 mm
- 1,50 x 1250,00 mm
- 2,00 x 1250,00 mm
- 3,00 x 1250,00 mm
Details at a glance
Chemical composition - limits in %
Al
0,30 - 0,70
Si
0,30 - 0,60
Nb
0,10 - 0,30
Fe
max. 0,20
O
max. 0,15
C
max. 0,08
N
max. 0,05
H
max. 0,013
Typical mechanical properties (from coil at room temperature) longitudinal section
0.2% Compressive strength
min. 320 MPa
Tensile strength
min. 438 MPa
Elongation
min. 33%
Typical mechanical properties (from coil at room temperature) landscape format
0.2% Compressive strength
min. 396 MPa
Tensile strength
min. 439 MPa
Elongation
min. 40%
Typical mechanical properties (from coil at room temperature) specification
0.2% Compressive strength
min. 215 MPa
Tensile strength
min. 340 MPa
Elongation
min. 20%