Titanium 6AL4V | 3.7165

ASTM B265

Ti-6Al4V Grade 5 was originally developed for aviation and aerospace applications. Due to the combination of excellent strength, low weight and excellent corrosion resistance, this alloy is now used in numerous applications, making it one of the most widely used titanium alloys today. It is also applied in the areas of sports, marine technology and medical technology. Another advantage of Ti-6Al4V Grade 5 when annealed is that it is suitable for use at temperatures up to 400°C and is easy to forge, form and weld.

 

Areas of application for Ti-6AL4V | WL 3.7165

Aircraft engine intake housings, compressor blades, disks, hubs and spacers, airframe components, offshore oil and gas equipment, power generation industry, motorsport/automotive components and consumer products.

Contact us if you have any questions.

S+D METALS Kontakt

Available from stock in the following dimensions

  • 6,00 mm
  • 8,00 mm
  • 10,00 mm
  • 12,00 mm
  • 15,00 mm
  • 20,00 mm
  • 25,00 mm
  • 30,00 mm
  • 35,00 mm
  • 40,00 mm
  • 45,00 mm
  • 50,00 mm
  • 60,00 mm

Details at a glance

Chemical composition - limits in %

Ti
Rest
Al
5,50 - 6,75
V
3,50 - 4,50
Fe
max. 0,30
O
max. 0,20

Physical constants and thermal properties

Density
4.42 g/cm³
Melting point
1648 °C
Beta transus temperature
980 ± 4°C
Thermal conductivity at 20°C
6.7 W/ m°C

Mechanical properties (room temperature)

Yield strength 0,30 - 6,00mm Thickness
min. 870 MPa
Yield strength 6,00 - 100,00mm Thickness
min. 830 MPa
Tensile strength 0,30 - 6,00mm Thickness
min. 920 MPa
Tensile strength 6,00 - 100,00mm Thickness
min. 900 MPa
Elongation
min. 10%